LEXAN?
135 resin
聚碳酸酯
產(chǎn)品說明:
General purpose low flow polycarbonate powder grade
|
材料狀態(tài)
|
|
|
資料 1
|
|
|
搜索 UL
黃卡
|
|
|
供貨地區(qū)
|
|
|
特性
|
|
|
用途
|
|
|
形式
|
|
|
加工方法
|
|
|
比重
|
|
|
ASTM
D792
|
|
--
|
1.20
|
g/cm?
|
|
|
--
|
1.19
|
g/cm?
|
|
|
熔流率（熔體流動速率） (300°C/1.2
kg)
|
3.5
|
g/10 min
|
ASTM
D1238
|
|
收縮率 - 流動 (3.20 mm)
|
0.50 到 0.70
|
%
|
內部方法
|
|
吸水率
|
|
|
ASTM
D570
|
|
平衡,
23°C
|
0.35
|
%
|
|
|
平衡,
100°C
|
0.58
|
%
|
|
|
抗張強度 2
|
|
|
ASTM
D638
|
|
屈服
|
62.0
|
MPa
|
|
|
斷裂
|
65.0
|
MPa
|
|
|
伸長率 2 (斷裂)
|
> 70
|
%
|
ASTM
D638
|
|
彎曲模量 3 (50.0 mm 跨距)
|
2340
|
MPa
|
ASTM
D790
|
|
彎曲強度 3 (屈服, 50.0 mm
跨距)
|
93.0
|
MPa
|
ASTM
D790
|
|
懸壁梁缺口沖擊強度 (23°C)
|
910
|
J/m
|
ASTM
D256
|
|
無缺口懸臂梁沖擊 (23°C)
|
無斷裂
|
|
ASTM
D4812
|
|
裝有測量儀表的落鏢沖擊 (23°C, Energy at Peak
Load)
|
64.0
|
J
|
ASTM
D3763
|
|
載荷下熱變形溫度
|
|
|
ASTM
D648
|
|
0.45 MPa,
未退火, 6.40 mm
|
137
|
°C
|
|
|
1.8 MPa,
未退火, 6.40 mm
|
132
|
°C
|
|
|
維卡軟化溫度
|
154
|
°C
|
ASTM
D1525 4
|
|
線形熱膨脹系數(shù) - 流動 (-40 到 95°C)
|
6.8E-5
|
cm/cm/°C
|
ASTM
E831
|
|
比熱
|
1250
|
J/kg/°C
|
ASTM
C351
|
|
透射率 (2540 ?m)
|
88.0
|
%
|
ASTM
D1003
|
|
霧度 (2540
?m)
|
1.0
|
%
|
ASTM
D1003
|
|
干燥溫度
|
121
|
°C
|
|
|
干燥時間
|
3.0 到 4.0
|
hr
|
|
|
干燥時間，最大
|
48
|
hr
|
|
|
建議的最大水分含量
|
0.020
|
%
|
|
|
建議注射量
|
40 到 60
|
%
|
|
|
料筒后部溫度
|
299 到 321
|
°C
|
|
|
料筒中部溫度
|
310 到 332
|
°C
|
|
|
料筒前部溫度
|
321 到 343
|
°C
|
|
|
射嘴溫度
|
316 到 338
|
°C
|
|
|
加工（熔體）溫度
|
321 到 343
|
°C
|
|
|
模具溫度
|
82.2 到 116
|
°C
|
|
|
背壓
|
0.345 到 0.689
|
MPa
|
|
|
螺桿轉速
|
40 到 70
|
rpm
|
|
|
排氣孔深度
|
0.025 到 0.076
|
mm
|
|