PBT/基礎(chǔ)創(chuàng)新塑料(美國) /4631原料描述：
|
密度 / 比重
|
1.67
|
g/cm?
|
ASTM D792, ISO 1183
|
|
熔流率（熔體流動速率）
|
|
|
ASTM D1238
|
|
250°C/2.16 kg
|
13
|
g/10 min
|
|
|
250°C/5.0 kg
|
67
|
g/10 min
|
|
|
265°C/5.0 kg
|
90
|
g/10 min
|
|
|
266°C/5.0 kg
|
90
|
g/10 min
|
|
|
熔融體積流量（MVR）
|
|
|
ISO 1133
|
|
250°C/5.0 kg
|
40
|
cm?/10min
|
|
|
265°C/5.0 kg
|
65
|
cm?/10min
|
|
|
收縮率 2
|
|
|
內(nèi)部方法
|
|
垂直
|
0.40 到 0.70
|
%
|
|
|
流動
|
0.10 到 0.30
|
%
|
|
|
吸水率
|
|
|
ISO 62
|
|
飽和, 23°C
|
0.25
|
%
|
|
|
平衡, 23°C, 50% RH
|
0.070
|
%
|
|
|
洛氏硬度 (R 計秤)
|
118
|
|
ISO 2039-2
|
|
球壓硬度 (H 358/30)
|
115
|
MPa
|
ISO 2039-1
|
|
拉伸模量
|
|
|
|
|
-- 3
|
11500
|
MPa
|
ASTM D638
|
|
--
|
11500
|
MPa
|
ISO 527-2/1
|
|
抗張強度
|
|
|
|
|
屈服 4
|
130
|
MPa
|
ASTM D638
|
|
屈服
|
130
|
MPa
|
ISO 527-2/5
|
|
斷裂 4
|
130
|
MPa
|
ASTM D638
|
|
斷裂
|
130
|
MPa
|
ISO 527-2/5
|
|
伸長率
|
|
|
|
|
屈服 4
|
2.0
|
%
|
ASTM D638
|
|
屈服
|
2.0
|
%
|
ISO 527-2/5
|
|
斷裂 4
|
2.0
|
%
|
ASTM D638
|
|
斷裂
|
2.0
|
%
|
ISO 527-2/5
|
|
彎曲模量
|
|
|
|
|
50.0 mm 跨距 5
|
9000
|
MPa
|
ASTM D790
|
|
-- 6
|
9600
|
MPa
|
ISO 178
|
|
彎曲應(yīng)力
|
|
|
|
|
-- 6, 7
|
200
|
MPa
|
ISO 178
|
|
屈服, 50.0 mm 跨距 5
|
200
|
MPa
|
ASTM D790
|
|
斷裂, 50.0 mm 跨距 5
|
200
|
MPa
|
ASTM D790
|
|
彎曲應(yīng)變 - at Break 8
|
3.0
|
%
|
ISO 178
|
|
簡支梁缺口沖擊強度
|
|
|
|
|
-30°C 9
|
10
|
kJ/m?
|
ISO 179/1eA
|
|
-30°C
|
9.0
|
kJ/m?
|
ISO 179/2C
|
|
23°C 9
|
10
|
kJ/m?
|
ISO 179/1eA
|
|
23°C
|
11
|
kJ/m?
|
ISO 179/2C
|
|
簡支梁無缺口沖擊強度
|
|
|
|
|
-30°C 9
|
55
|
kJ/m?
|
ISO 179/1eU
|
|
-30°C
|
50
|
kJ/m?
|
ISO 179/2U
|
|
23°C 9
|
50
|
kJ/m?
|
ISO 179/1eU, ISO 179/2U
|
|
懸壁梁缺口沖擊強度
|
|
|
|
|
-30°C
|
80
|
J/m
|
ASTM D256
|
|
0°C
|
80
|
J/m
|
ASTM D256
|
|
23°C
|
80
|
J/m
|
ASTM D256
|
|
-30°C 10
|
8.0
|
kJ/m?
|
ISO 180/1A
|
|
0°C 10
|
8.0
|
kJ/m?
|
ISO 180/1A
|
|
23°C 10
|
8.0
|
kJ/m?
|
ISO 180/1A
|
|
無缺口懸臂梁沖擊
|
|
|
|
|
-30°C
|
660
|
J/m
|
ASTM D4812
|
|
23°C
|
660
|
J/m
|
ASTM D4812
|
|
-30°C 10
|
45
|
kJ/m?
|
ISO 180/1U
|
|
23°C 10
|
45
|
kJ/m?
|
ISO 180/1U
|
|
載荷下熱變形溫度
|
|
|
|
|
0.45 MPa, 未退火, 3.20 mm
|
220
|
°C
|
ASTM D648
|
|
0.45 MPa, 未退火, 4.00 mm, 100 mm 跨距 11
|
220
|
°C
|
ISO 75-2/Be
|
|
0.45 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 10
|
220
|
°C
|
ISO 75-2/Bf
|
|
1.8 MPa, 未退火, 3.20 mm
|
205
|
°C
|
ASTM D648
|
|
1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 10
|
205
|
°C
|
ISO 75-2/Af
|
|
維卡軟化溫度
|
|
|
|
|
--
|
220
|
°C
|
ASTM D1525 12, ISO 306/A50 12
|
|
--
|
205
|
°C
|
ASTM D1525 13, ISO 306/B50, ISO 306/B120
|
|
Ball Pressure Test (123 到 127°C)
|
通過
|
|
IEC 60695-10-2
|
|
線形熱膨脹系數(shù)
|
|
|
ISO 11359-2
|
|
流動 : -40 到 40°C
|
2.2E-5
|
cm/cm/°C
|
|
|
流動 : 23 到 80°C
|
1.6E-5
|
cm/cm/°C
|
|
|
流動 : 23 到 150°C
|
1.4E-5
|
cm/cm/°C
|
|
|
垂直 : -40°C
|
8.2E-5
|
cm/cm/°C
|
|
|
垂直 : 23 到 80°C
|
1.2E-4
|
cm/cm/°C
|
|
|
垂直 : 23 到 150°C
|
1.3E-4
|
cm/cm/°C
|
|
|
RTI Elec
|
130
|
°C
|
UL 746
|
|
RTI Imp
|
130
|
°C
|
UL 746
|
|
RTI
|
140
|
°C
|
UL 746
|
|
表面電阻率
|
> 1.0E+15
|
ohms
|
IEC 60093
|
|
體積電阻率
|
> 1.0E+15
|
ohms·cm
|
ASTM D257, IEC 60093
|
|
介電強度
|
|
|
IEC 60243-1
|
|
0.800 mm, 在油中
|
27
|
kV/mm
|
|
|
1.60 mm, 在油中
|
23
|
kV/mm
|
|
|
3.20 mm, 在油中
|
19
|
kV/mm
|
|
|
介電常數(shù)
|
|
|
|
|
1 MHz
|
3.50
|
|
ASTM D150, IEC 60250
|
|
50 Hz
|
3.00
|
|
IEC 60250
|
|
60 Hz
|
3.00
|
|
IEC 60250
|
|
耗散因數(shù)
|
|
|
|
|
1 MHz
|
0.010
|
|
ASTM D150, IEC 60250
|
|
50 Hz
|
1.0E-3
|
|
IEC 60250
|
|
60 Hz
|
1.0E-3
|
|
IEC 60250
|
|
相比耐漏電起痕指數(shù)(CTI)
|
PLC 2
|
|
UL 746
|
|
漏電起痕指數(shù)
|
250
|
V
|
IEC 60112
|
|
高電弧燃燒指數(shù)(HAI) 14
|
PLC 3
|
|
UL 746
|
|
高電壓電弧起痕速率 (HVTR)
|
PLC 4
|
|
UL 746
|
|
熱絲引燃 (HWI)
|
PLC 0
|
|
UL 746
|
|
UL 阻燃等級 (0.75 mm)
|
V-0
|
|
UL 94
|
|
灼熱絲易燃指數(shù) (3.0 mm)
|
960
|
°C
|
IEC 60695-2-12
|
|
極限氧指數(shù)
|
34
|
%
|
ISO 4589-2
|
|
熔體粘度 (260°C, 1500 sec^-1)
|
115
|
Pa·s
|
ISO 11443
|
|
填充物
|
30
|
%
|
ASTM D229
|
|
干燥溫度
|
110 到 120
|
°C
|
|
|
干燥時間
|
2.0 到 4.0
|
hr
|
|
|
建議的最大水分含量
|
0.020
|
%
|
|
|
料斗溫度
|
40 到 60
|
°C
|
|
|
料筒后部溫度
|
230 到 245
|
°C
|
|
|
料筒中部溫度
|
240 到 255
|
°C
|
|
|
料筒前部溫度
|
245 到 265
|
°C
|
|
|
射嘴溫度
|
240 到 260
|
°C
|
|
|
加工（熔體）溫度
|
250 到 270
|
°C
|
|
|
模具溫度
|
40 到 100
|
°C
|
|