6555 PC 上？扑紕(chuàng)（拜耳）產(chǎn)品詳細描述：
|
密度 (23°C)
|
1.20
|
g/cm?
|
ISO 1183
|
|
表觀密度 3
|
0.64
|
g/cm?
|
ISO 60
|
|
熔流率（熔體流動速率） (300°C/1.2 kg)
|
10
|
g/10 min
|
ISO 1133
|
|
熔融體積流量（MVR） (300°C/1.2 kg)
|
10.0
|
cm?/10min
|
ISO 1133
|
|
收縮率
|
|
|
|
|
橫向流量
|
0.60 到 0.80
|
%
|
ISO 2577
|
|
流量
|
0.60 到 0.80
|
%
|
ISO 2577
|
|
橫向流量 : 280°C, 2.00 mm 4
|
0.75
|
%
|
ISO 294-4
|
|
流量 : 2.00 mm 4
|
0.70
|
%
|
ISO 294-4
|
|
吸水率
|
|
|
ISO 62
|
|
飽和, 23°C
|
0.30
|
%
|
|
|
平衡, 23°C, 50% RH
|
0.12
|
%
|
|
|
球壓硬度
|
115
|
MPa
|
ISO 2039-1
|
|
拉伸模量 (23°C)
|
2400
|
MPa
|
ISO 527-2/1
|
|
拉伸應(yīng)力
|
|
|
ISO 527-2/50
|
|
屈服, 23°C
|
66.0
|
MPa
|
|
|
斷裂, 23°C
|
70.0
|
MPa
|
|
|
拉伸應(yīng)變
|
|
|
ISO 527-2/50
|
|
屈服, 23°C
|
6.2
|
%
|
|
|
斷裂, 23°C
|
130
|
%
|
|
|
標稱拉伸斷裂應(yīng)變 (23°C)
|
> 50
|
%
|
ISO 527-2/50
|
|
拉伸蠕變模量
|
|
|
ISO 899-1
|
|
1 hr
|
2200
|
MPa
|
|
|
1000 hr
|
1900
|
MPa
|
|
|
彎曲模量 5 (23°C)
|
2400
|
MPa
|
ISO 178
|
|
彎曲應(yīng)力 5
|
|
|
ISO 178
|
|
23°C
|
98.0
|
MPa
|
|
|
3.5% 應(yīng)變, 23°C
|
74.0
|
MPa
|
|
|
Flexural Strain at Flexural Strength 6 (23°C)
|
7.1
|
%
|
ISO 178
|
|
水氣透過率 (23°C, 85% RH, 100 ?m)
|
15
|
g/m?/24 hr
|
ISO 15106-1
|
|
Carbon Dioxide Permeability (23°C, 25.4 ?m)
|
16900
|
cm?/m?/bar/24 hr
|
ISO 2556
|
|
Gas Permeation
|
|
|
ISO 2556
|
|
Carbon Dioxide : 100.0 ?m
|
4300
|
cm?/m?/bar/24 hr
|
|
|
Nitrogen : 25.4 ?m
|
510
|
cm?/m?/bar/24 hr
|
|
|
Nitrogen : 100.0 ?m
|
130
|
cm?/m?/bar/24 hr
|
|
|
Oxygen : 25.4 ?m
|
2760
|
cm?/m?/bar/24 hr
|
|
|
Oxygen : 100.0 ?m
|
700
|
cm?/m?/bar/24 hr
|
|
|
簡支梁缺口沖擊強度 7
|
|
|
ISO 179/1eA
|
|
-30°C, 完全斷裂
|
14
|
kJ/m?
|
|
|
23°C, 局部斷裂
|
70
|
kJ/m?
|
|
|
簡支梁無缺口沖擊強度
|
|
|
ISO 179/1eU
|
|
-60°C
|
無斷裂
|
|
|
|
-30°C
|
無斷裂
|
|
|
|
23°C
|
無斷裂
|
|
|
|
懸壁梁缺口沖擊強度 7
|
|
|
ISO 180/A
|
|
-30°C, 完全斷裂
|
12
|
kJ/m?
|
|
|
23°C, 局部斷裂
|
65
|
kJ/m?
|
|
|
多軸向儀器化沖擊能量
|
|
|
ISO 6603-2
|
|
-30°C
|
65.0
|
J
|
|
|
23°C
|
60.0
|
J
|
|
|
多軸向儀器化沖擊力峰值
|
|
|
ISO 6603-2
|
|
-30°C
|
6300
|
N
|
|
|
23°C
|
5400
|
N
|
|
|
熱變形溫度
|
|
|
|
|
0.45 MPa, 未退火
|
137
|
°C
|
ISO 75-2/B
|
|
1.8 MPa, 未退火
|
125
|
°C
|
ISO 75-2/A
|
|
玻璃轉(zhuǎn)化溫度 8
|
145
|
°C
|
ISO 11357-2
|
|
維卡軟化溫度
|
|
|
|
|
--
|
144
|
°C
|
ISO 306/B50
|
|
--
|
145
|
°C
|
ISO 306/B120
|
|
Ball Pressure Test (136°C)
|
通過
|
|
IEC 60695-10-2
|
|
線形熱膨脹系數(shù)
|
|
|
ISO 11359-2
|
|
流動 : 23 到 55°C
|
6.5E-5
|
cm/cm/°C
|
|
|
橫向 : 23 到 55°C
|
6.5E-5
|
cm/cm/°C
|
|
|
導(dǎo)熱系數(shù) 9 (23°C)
|
0.20
|
W/m/K
|
ISO 8302
|
|
RTI Elec (1.5 mm)
|
125
|
°C
|
UL 746
|
|
RTI Imp (1.5 mm)
|
115
|
°C
|
UL 746
|
|
RTI (1.5 mm)
|
125
|
°C
|
UL 746
|
|
表面電阻率
|
1.0E+16
|
ohms
|
IEC 60093
|
|
體積電阻率 (23°C)
|
1.0E+16
|
ohms·cm
|
IEC 60093
|
|
介電強度 (23°C, 1.00 mm)
|
34
|
kV/mm
|
IEC 60243-1
|
|
相對電容率
|
|
|
IEC 60250
|
|
23°C, 100 Hz
|
3.10
|
|
|
|
23°C, 1 MHz
|
3.00
|
|
|
|
耗散因數(shù)
|
|
|
IEC 60250
|
|
23°C, 100 Hz
|
8.0E-4
|
|
|
|
23°C, 1 MHz
|
9.0E-3
|
|
|
|
漏電起痕指數(shù)
|
|
|
IEC 60112
|
|
解決方案 A
|
225
|
V
|
|
|
解決方案 B
|
125
|
V
|
|
|
UL 阻燃等級
|
|
|
UL 94
|
|
1.0 mm
|
V-2
|
|
|
|
3.0 mm
|
V-0
|
|
|
|
灼熱絲易燃指數(shù)
|
|
|
IEC 60695-2-12
|
|
0.75 mm
|
875
|
°C
|
|
|
1.5 mm
|
960
|
°C
|
|
|
3.0 mm
|
960
|
°C
|
|
|
熱燈絲點火溫度
|
|
|
IEC 60695-2-13
|
|
0.75 mm
|
875
|
°C
|
|
|
1.5 mm
|
875
|
°C
|
|
|
3.0 mm
|
875
|
°C
|
|
|
極限氧指數(shù) 10
|
35
|
%
|
ISO 4589-2
|
|
Application of Flame from Small Burner 11
|
K1, F1
|
|
DIN 53438-1, -3
|
|
Flash Ignition Temperature
|
460
|
°C
|
ASTM D1929
|
|
Glow Wire Test
|
|
|
EDF HN60 E.02
|
|
1.50 mm
|
750
|
°C
|
|
|
3.00 mm
|
750
|
°C
|
|
|
Needle Flame Test
|
|
|
IEC 60695-11-5
|
|
1.50 mm 12
|
2.0
|
min
|
|
|
1.50 mm 13
|
1.0
|
min
|
|
|
2.00 mm 12
|
2.0
|
min
|
|
|
2.00 mm 13
|
2.0
|
min
|
|
|
3.00 mm 13
|
2.0
|
min
|
|
|
3.00 mm 12
|
2.0
|
min
|
|
|
Self Ignition Temperature
|
530
|
°C
|
ASTM D1929
|
|
燃燒速率 14 (> 1.00 mm)
|
passed
|
|
ISO 3795
|
|
折射率 15
|
1.586
|
|
ISO 489
|
|
透射率
|
|
|
ISO 13468-2
|
|
1000 ?m
|
89.0
|
%
|
|
|
2000 ?m
|
89.0
|
%
|
|
|
3000 ?m
|
88.0
|
%
|
|
|
4000 ?m
|
87.0
|
%
|
|
|
Electrolytical Corrosion (23°C)
|
A1
|
|
IEC 60426
|
|
ISO Shortname
|
ISO 7391-PC,MFR,(,,)-09-9
|
|
|
|
干燥溫度 - Dry Air Dryer
|
120
|
°C
|
|
|
干燥時間 - Dry Air Dryer
|
4.0
|
hr
|
|
|
建議的最大水分含量
|
< 0.020
|
%
|
|
|
建議注射量
|
30 到 70
|
%
|
|
|
料筒后部溫度
|
250 到 270
|
°C
|
|
|
料筒中部溫度
|
270 到 290
|
°C
|
|
|
料筒前部溫度
|
285 到 305
|
°C
|
|
|
射嘴溫度
|
270 到 305
|
°C
|
|
|
加工（熔體）溫度
|
280 到 320
|
°C
|
|
|
模具溫度
|
70 到 110
|
°C
|
|
|
背壓
|
10.0 到 20.0
|
MPa
|
|
|
排氣孔深度
|
0.025 到 0.075
|
mm
|
購買須知：1)因塑膠價格波動頻繁，網(wǎng)頁上的報價可能會與當天實際報價有所差異，請用QQ或電話直接詢價。感謝您的大力支持！
2)銷售說明：本公司可支持多種原料混搭訂購,25公斤/包起訂,批量可折扣,款到發(fā)貨（東莞周邊城市可貨到付款).可提供正規(guī)（17%）增值稅，提供售前咨詢，售后服務(wù)，并由專業(yè)工程師提供一對一的產(chǎn)品問題解決方案。
3) 鄭重承諾:到貨時間：珠三角地區(qū)一天內(nèi)到達,國內(nèi)各地3-4天到貨.本公司所售原料均為原廠原包裝正牌料，為了維護廣大客戶的利益，本公司杜絕一切副牌料,以次充好.歡迎來電垂詢！
|
在線咨詢 