The non copper coated OK AristoRod 12.52 is a manganese-silicon alloyed solid wire for GMAW of unalloyed steels, such as general structural, pressure vessel, ship building and for fine-grained carbon-manganese steels for the same purpose with a minimum yield strength of 420 MPa. The AristoRod wires are suitable for operating at high currents with maintained disturbance free wire feeding giving a stable arc with a low amount of spatter. OK AristoRod 12.52 can be delivered in the unique ESAB Marathon Pac,which is an excellent chioce in mechanised welding applications.
典型拉伸性能
|
As welded
|
|
保護氣體
|
屈服強度
|
延伸率
|
抗拉強度
|
Stress Relieved Temperature
|
Stress Relieved Testing Time
|
|
EN 80Ar20CO2(M21)
|
480 MPa
|
26 %
|
560 MPa
|
-
|
-
|
|
Stress relieved
|
|
保護氣體
|
屈服強度
|
延伸率
|
抗拉強度
|
Stress Relieved Temperature
|
Stress Relieved Testing Time
|
|
EN 80Ar20CO2(M21)
|
380 MPa
|
28 %
|
495 MPa
|
620 °C
|
15 hr
|
夏比V型缺口沖擊性能
|
As welded
|
|
保護氣體
|
沖擊值
|
測試溫度
|
Stress Relieved Testing Temp
|
Stress Relieved Testing Time
|
|
EN 80Ar20CO2(M21)
|
130 J
|
20 °C
|
-
|
-
|
|
EN 80Ar20CO2(M21)
|
90 J
|
-20 °C
|
-
|
-
|
|
EN 80Ar20CO2(M21)
|
70 J
|
-30 °C
|
-
|
-
|
|
EN 80Ar20CO2(M21)
|
60 J
|
-40 °C
|
-
|
-
|
|
Stress relieved
|
|
保護氣體
|
沖擊值
|
測試溫度
|
Stress Relieved Testing Temp
|
Stress Relieved Testing Time
|
|
EN 80Ar20CO2(M21)
|
120 J
|
20 °C
|
620 °C
|
15 hr
|
|
EN 80Ar20CO2(M21)
|
90 J
|
-20 °C
|
620 °C
|
15 hr
|
焊縫金屬分析
|
Mn
|
C
|
Si
|
Ti+Zr
|
|
1.46 %
|
0.08 %
|
0.85 %
|
<0,01 %
|
熔敷數(shù)據(jù)
|
安培
|
熔敷率
|
電壓 V
|
直徑
|
送絲速度
|
|
60-200 A
|
0.8-2.3 kg/h
|
18-24 V
|
0.8 mm
|
3.2-10 m/min
|
|
70-250 A
|
0.9-3.5 kg/h
|
18-26 V
|
0.9 mm
|
3.0-12 m/min
|
|
80-300 A
|
1.0-5.5 kg/h
|
18-32 V
|
1.0 mm
|
2.7-15 m/min
|
|
120-380 A
|
1.3-8.0 kg/h
|
18-35 V
|
1.2 mm
|
2.5-15 m/min
|
|
150-420 A
|
1.6-8.7 kg/h
|
22-36 V
|
1.4 mm
|
2.3-12 m/min
|
|
225-550 A
|
2.1-9.4 kg/h
|
28-38 V
|
1.6 mm
|
2.3-10 m/min
|
|
認(rèn)證:
|
YGW16 (M21), JIS
|
|
分類:
|
G 42 4 M21 3Si1, EN ISO 14341-A, Weld Metal, G 3Si1, EN ISO 14341-A, Wire Electrode, ER70S-G, SFA/AWS A5.18, Wire Electrode, YGW 16 (M21), (items ending with H), JIS Z 3312, Wire Electrode
|
認(rèn)證均基于工廠的所在地。如需更多信息，請聯(lián)系伊薩。
|
合金類型:
|
Carbon-manganese steel (Mn/Si-alloyed)
|
|