適用于最小抗拉強度690 MPa高強度鋼GTAW焊接的鍍銅低合金鉻鎳鉬(0,5% Cr, 0,5% Ni, 0,2% Mo)焊絲。該焊絲也適用于焊接低溫條件下需要具有良好沖擊強度的鋼種。
典型拉伸性能
|
As welded
|
|
保護氣體
|
屈服強度
|
延伸率
|
抗拉強度
|
Stress Relieved Temperature
|
Stress Relieved Testing Time
|
|
Ar(I1) AWS
|
636 MPa
|
16 %
|
713 MPa
|
-
|
-
|
|
Ar (I1) EN
|
720 MPa
|
21 %
|
817 MPa
|
-
|
-
|
|
Stress relieved
|
|
保護氣體
|
屈服強度
|
延伸率
|
抗拉強度
|
Stress Relieved Temperature
|
Stress Relieved Testing Time
|
|
Ar (I1) EN
|
629 MPa
|
23 %
|
716 MPa
|
620 °C
|
2 hr
|
夏比V型缺口沖擊性能
|
As welded
|
|
保護氣體
|
沖擊值
|
測試溫度
|
Stress Relieved Testing Temp
|
Stress Relieved Testing Time
|
|
Ar(I1) AWS
|
123 J
|
-30 °C
|
-
|
-
|
|
Ar(I1) AWS
|
86 J
|
-40 °C
|
-
|
-
|
|
Ar (I1) EN
|
129 J
|
-30 °C
|
-
|
-
|
|
Ar (I1) EN
|
120 J
|
-40 °C
|
-
|
-
|
|
Stress relieved
|
|
保護氣體
|
沖擊值
|
測試溫度
|
Stress Relieved Testing Temp
|
Stress Relieved Testing Time
|
|
Ar (I1) EN
|
140 J
|
-30 °C
|
620 °C
|
2 hr
|
|
Ar (I1) EN
|
79 J
|
-40 °C
|
620 °C
|
2 hr
|
焊縫金屬分析
|
Mn
|
Mo
|
C
|
Si
|
Ni
|
Cr
|
|
1.38 %
|
0.19 %
|
0.118 %
|
0.71 %
|
0.52 %
|
0.57 %
|
|
分類:
|
W 55 4 Mn3NiCrMo, EN ISO 16834-A, Mn3NiCrMo, EN ISO 16834-A, Wire Electrode, ER100S-G, SFA/AWS A5.28, Wire Electrode
|
|
合金類型:
|
Low alloyed steel (0.5 % Cr - 0.5 % Ni - 0.2 % Mo)
|
|