| 性能項(xiàng)目 | 試驗(yàn)條件[狀態(tài)] | 測(cè)試方法 | 測(cè)試數(shù)據(jù) | 數(shù)據(jù)單位 |
| 物理性能 | 比重 |
| ASTMD792 | 1.19 | g/cm3 |
| 密度 |
| ISO1183 | 1.20 | g/cm3 |
| 熔流率（熔體流動(dòng)速率）(300°C/1.2kg) |
| ASTMD1238 | 18 | g/10min |
| 溶化體積流率（MVR）(300°C/1.2kg) |
| ISO1133 | 17.0 | cm3/10min |
| 收縮率-流動(dòng)(3.20mm) |
| InternalMethod | 0.55to0.75 | |
| MoldingShrinkage-AcrossFlow(3.20mm) |
| InternalMethod | 0.60to0.80 | |
| 吸水率(飽和,23°C) |
| ISO62 | 0.13 | |
| 吸水率(平衡,23°C,50RH) |
| ISO62 | 0.11 | |
| 機(jī)械性能 | 拉伸模量2 |
| ASTMD638 | 2400 | MPa |
| 拉伸模量 |
| ISO527-2/1 | 2300 | MPa |
| 抗張強(qiáng)度3(屈服) |
| ASTMD638 | 67.0 | MPa |
| 拉伸應(yīng)力(屈服) |
| ISO527-2/50 | 63.0 | MPa |
| 抗張強(qiáng)度3(斷裂) |
| ASTMD638 | 54.0 | MPa |
| 拉伸應(yīng)力(斷裂) |
| ISO527-2/50 | 57.0 | MPa |
| 伸長(zhǎng)率3(屈服) |
| ASTMD638 | 6.0 | |
| 拉伸應(yīng)變(屈服) |
| ISO527-2/50 | 6.0 | |
| 伸長(zhǎng)率4(斷裂) |
| ASTMD638 | 80 | |
| 拉伸應(yīng)變(斷裂) |
| ISO527-2/50 | 73 | |
| 彎曲模量4(50.0mm跨距) |
| ASTMD790 | 2400 | MPa |
| 彎曲模量5 |
| ISO178 | 2400 | MPa |
| FlexuralStress5,6 |
| ISO178 | 96.0 | MPa |
| 彎曲強(qiáng)度4(屈服,50.0mm跨距) |
| ASTMD790 | 103 | MPa |
| 沖擊性能 | 簡(jiǎn)支梁缺口沖擊強(qiáng)度7 | -30°C | ISO179/1eA | 9.0 | kJ/m2 |
| 23°C | ISO179/1eA | 10 | kJ/m2 |
| 簡(jiǎn)支梁無(wú)缺口沖擊強(qiáng)度7 | -30°C | ISO179/1eU | NoBreak |
|
| 23°C | ISO179/1eU | NoBreak |
|
| 懸壁梁缺口沖擊強(qiáng)度 | -30°C | ASTMD256 | 85 | J/m |
| 23°C | ASTMD256 | 100 | J/m |
| 懸壁梁缺口沖擊強(qiáng)度8 | -30°C | ISO180/1A | 9.0 | kJ/m2 |
| 23°C | ISO180/1A | 10 | kJ/m2 |
| 懸壁梁缺口沖擊強(qiáng)度 | -30°C | ASTMD4812 | NoBreak |
|
| 23°C | ASTMD4812 | NoBreak |
|
| 無(wú)缺口伊佐德沖擊強(qiáng)度8 | -30°C | ISO180/1U | NoBreak |
|
| 23°C | ISO180/1U | NoBreak |
|
| 裝有測(cè)量?jī)x表的落鏢沖擊(23°C,TotalEnergy) |
| ASTMD3763 | 65.0 | J |
| 熱性能 | 載荷下熱變形溫度(0.45MPa,未退火,3.20mm) |
| ASTMD648 | 130 | °C |
| HeatDeflectionTemperature9(0.45MPa,Unannealed,100mmSpan) |
| ISO75-2/Be | 131 | °C |
| 載荷下熱變形溫度(1.8MPa,未退火,3.20mm) |
| ASTMD648 | 120 | °C |
| HeatDeflectionTemperature9(1.8MPa,Unannealed,100mmSpan) |
| ISO75-2/Ae | 121 | °C |
| 維卡軟化溫度 |
| ASTMD152510 | 136 | °C |
| -- | ISO306/B50 | 139 | °C |
| -- | ISO306/B120 | 140 | °C |
| BallPressureTest(125°C) |
| IEC60695-10-2 | Pass |
|
| 線形熱膨脹系數(shù)-流動(dòng)(-40到40°C) |
| ASTME831 | 6.8E-5 | cm/cm/°C |
| 線形熱膨脹系數(shù)-流動(dòng)(23到80°C) |
| ISO11359-2 | 7.7E-5 | cm/cm/°C |
| 線形熱膨脹系數(shù)-橫向(-40到40°C) |
| ASTME831 | 7.0E-5 | cm/cm/°C |
| CLTE-Transverse(23to80°C) |
| ISO11359-2 | 8.0E-5 | cm/cm/°C |
| RTIElec |
| UL746 | 130 | °C |
| RTIImp |
| UL746 | 120 | °C |
| RTIStr |
| UL746 | 130 | °C |
| 電氣性能 | 介電常數(shù)(1.10GHz) |
| ASTMES7-83 | 2.78 |
|
| 耗散因數(shù)(1.10GHz) |
| ASTMES7-83 | 5.6E-3 |
|
| 可燃性 | UL阻燃等級(jí) | 0.40mm | UL94 | V-2
|