Jupiter B TIG氬弧焊絲
Gas Tungsten Arc Welding(GTAW)
For cast irons and cast iron to steels. Joining and Build up. 用于鑄鐵以及鑄鐵和鋼的焊接和堆焊。
Features 亮點
High Strength 60,000 psi/414MPa
抗拉強度高達60,000 psi/414MPa
High Nickel Content
鎳含量高
Fully Machinable
完全可加工
Repairs Cracks
修復裂縫
Cast Iron to Steel Joints
鑄鐵-鋼連接
Porosity Free Deposits
無孔隙熔敷物
Build Up Worn Areas
堆焊磨損區(qū)域
Easy To Use
易于使用
Characteristics 特點
Jupiter B TIG is a versatile inert arc filler metal specially suited for use on all cast iron parts or for joining cast iron to steel. Deposits are strong, dense and fully machinable. No special techniques are required for this easy to apply product. When repairing critical cast iron components such as valves, pumps, blocks or machine housings Jupiter B TIG assists the welder in producing high quality welds with minimum time and effort.
Jupiter B TIG是一種通用的鑄鐵氬弧焊絲，特別適用于所有鑄鐵零件的焊接或?qū)㈣T鐵與鋼連接。熔敷物堅固、致密且完全可加工。易于使用，不需要特殊的技巧。在修理閥門、泵、缸體或機器外殼等關鍵鑄鐵部件時，Jupiter B TIG有助于焊工用最少的時間和精力生產(chǎn)出高質(zhì)量的焊縫。
Technical技術規(guī)格
|
Inches |
1/16 |
3/32 |
1/8 |
|
(mm) |
(1.6) |
(2.4) |
(3.2) |
(AC with Hi-Frequency)
Best Practices Application 應用
Use DC straight polarity with argon. Adjust cup, tungsten and amperage to suit metal thickness.
使用氬氣直流正接。調(diào)整保護罩，鎢極以及電流以適應母材厚度。
Clean base metal. Remove all grease and other contamination from repair area.
清潔母材。
Remove sharp edges or protrusions in the base metal.
去除母材中的鋒利邊緣或突起。
For machinability or critical parts preheat to 500?F(260?C).
對于可加工性或關鍵零件，預熱至500?F（260?C）。
Backstep to fill crater before withdrawing.
收弧前退焊以填滿弧坑
Cool slowly after welding and light peening are recommended.
推薦焊后緩冷及輕敲擊。